| Flooring Radiant Panel |
ASTM E648; NBSIR 75-950; NFPA 253, Critical Radiant Flux |
0.73 W/cm², Class I |
| Resistance to Light Fading |
ISO |
6 8 good (indoor use) |
| Residual Indentation |
LF-475A |
.002" average |
| Residual Indentation |
EN 433 |
.04mm |
| Abrasive Wear, Taber 1000 gm weight |
H-18 wheels, 5000 cycles |
1.1% loss of weight |
| Abrasive Wear, Taber 1000 gm weight |
H-18 wheels, to wear layer penetration |
>25,700 cycles, (2.1% loss of weight) |
| Static Coefficient of Friction |
ASTM D-2047-03 James Test |
.5 approx |
| Static Coefficient Of Friction (www.nfsi.org) |
B101.1 ANSI/NFSI Standard Test Method for Measuring Wet SCOF |
High Traction >0.60 Certified |
| Static Coefficient of Friction |
ASTM C-1028-89 dynamometer pull method |
Not rated |
| Shore Hardness |
91 |
| Static Load Limit |
DIN 16961.2 |
>350 p.s.i. |
| Volume Resisitivity |
NFPA 99 |
<2x1011 ohms (not waxed) |
| Electrostatic Propensity |
AATCC 134 |
Neolite step +5.3KV;
Neolite scuff +6.0 kV;
SD polyurethane step 0.2KV;
SD polyurethane scuff 0.7KV |
| Chemical Resistance |
Very good to most diluted acids, alkalis and common detergents. Some solvents can swell or dissolve vinyl. (Request detailed information from manufacturer). |
| Staining or permanent discoloration |
Not resistant to rubber (yellowing from certain antioxidants, oil based grease, tar based asphalt, lipstick |
| Charge Decay Time |
FTMS 4046-101c |
<<<.17 seconds |
| Flammability |
Radiant Panel ASTM E648 |
.73W/cm², Class I |
| Euro-flex™ meets or exceeds all requirements of Federal Specifications LF-475a and SST-312b for dimensional stability, flexibility, resistance to reagents and residual indentation |
| Short Form Specifications |
Staining or permanent discoloration Not resistant to rubber (yellowing from certain antioxidants, oil based grease, tar based asphalt, lipstick |